Recycled high impact polystyrene
MFI:
4.6
r HIPS GON-HB4
Recycled high impact polystyrene
HIPS-HB4 is recycled white high impact polystyrene resin featuring uniform color, high purity and low impurity content. It delivers balanced tensile, flexural and impact mechanical performance alongside stable melt flow under standard lab conditions (23℃, 50% RH), perfectly fit for common extrusion and injection molding manufacturing.
PRODUCTS PARAMETERS
PROPERTIES | TEST STANDARDS | TEST CONDITIONS | S.I. UNITS | TECHNICAL VALUES |
Melting Flow Rate | GB/T 3682.1 | 230℃/2.16 Kg | g/10min | 7.6 |
Tensile Strength | GB/T 1040.2 | 50mm/min | MPa | 36 |
Flexural Strength | GB/T 9341 | 2mm/min | MPa | 64 |
Flexural Modulus | GB/T 9341 | 2mm/min | MPa | 2648.5 |
Impact Strength | GB/T 1843 | 23℃ | KJ/m³ | 5 |
Elongation at Break | GB/T 1040.2 | 50mm/min | % | 39.2 |