Our homopolymer chemical recycled PP series includes Alprene RPP-H G3103, RPP-H G150 and RPP-H G3117. Manufactured via liquid-phase bulk polymerization from chemically recycled waste plastic propylene, these eco-friendly rPP grades feature low odor, stable mechanical rigidity and clean appearance. Support food-contact compliance, covering film extrusion, fiber drawing, general injection molding, household goods and toy production.
No slip agent & no opening agent, pure formulation
Stable isotactic index and low ash content
Chemical recycled material with eco-friendly performance
Model 2: RPP-H G150
White, odorless, non-toxic and lightweight thermoplastic material
Excellent chemical stability, resistant to acid and alkali corrosion
Superior plasticity and reliable heat resistance
High flexural modulus for good structural rigidity
Eco-friendly chemical recycled PP from waste plastic feedstock
Complies with SH/T 1761.1-2019 industry standard
Model 3: RPP-H G3117
High transparency for bright clear finished parts
Good stiffness, high tensile yield strength and flexural modulus
Low odor, suitable for daily contact products
No opening agent & no smooth agent, pure clean formulation
Stable isotactic index and moderate ash content
High heat deflection temperature with excellent heat resistance
Eco-friendly chemical recycling PP raw material
PRODUCTS PARAMETERS
Model 1: RPP-H G3103
RPP-H G3103 is chemical recycling homopolymer PP without slip agent or opening agent. It delivers low precipitation, low odor and high rigidity, designed for food-contact film, lunch box extrusion and fiber spinning.
Typical Property
Test Method
Unit
Value
Melt flow rate (230℃, 2.16kg)
GB/T 3682.1-2018
g/10min
3.2
Density
GB/T 1033-2008
g/cm³
0.903
Tensile strength at yield
GB/T 1040.2-2022
MPa
32
Tensile Stress at Break
GB/T 1040.2-2022
MPa
20
Heat Deflection Temperature (Tf0.45)
GB/T 1634.2-2009
℃
78
Model 2: RPP-H G150
RPP-H G150 is liquid-phase bulk polymerized chemical recycled homopolymer PP resin. It is white, odorless, non-toxic lightweight thermoplastic with excellent acid-alkali corrosion resistance, great plasticity and heat resistance, mainly used for injection molding and modified compounding.
Typical Property
Test Method
Unit
Value
Melt flow rate (230℃, 2.16kg)
GB/T 3682.1
g/10min
19
Density
GB/T 9345.1
g/cm³
0.905
Tensile strength at yield
GB/T 1040.2-2022
MPa
28
Charpy Impact Strength (23℃)
GB/T 1043.1-2008
kJ/m²
2.3
Flexural modulus
GB/T 9341
MPa
1417
Model 3: RPP-H G3117
RPP-H G3117 is chemical recycled homopolymer polypropylene without opening agent or smooth agent. It owns high transparency, good rigidity and low odor, ideal for transparent injection molded household goods and plastic toys.
Typical Property
Test Method
Unit
Value
Melt flow rate (230℃, 2.16kg)
GB/T 3682.1
g/10min
17
Density
GB/T 1033
g/cm³
0.905
Tensile strength at yield
GB/T 1040.2-2022
MPa
32.6
Charpy Impact Strength
GB/T 1043.1-2008
kJ/m²
1.8
Heat Deflection Temperature (Tf0.45)
GB/T 1634.2-2009
℃
85
PRODUCTS APPLICATION
Model 1: RPP-H G3103
Extrusion: Food-grade lunch boxes
Fiber drawing & textile yarn production
Film production: BOPP and CPP packaging films
Model 2: RPP-H G150
General injection-molded plastic finished goods
Modified compound for compression molding production
Electrical appliance & automotive plastic parts
Mechanical components, TV & audio equipment casings